标准号:SAE AMS 6327K-2012
中文标准名称:热处理,抗拉强度125 ksi (862 MPa)0.50Cr 0.55Ni 0.25Mo (0.38 0.43C) (SAE 8740)钢筋和钢锻件
英文标准名称:Steel Bars and Forgings 0.50Cr 0.55Ni 0.25Mo (0.38 0.43C) (SAE 8740) Heat Treated, 125 ksi (862 MPa) Tensile Strength
标准类型:V11
发布日期:2012/10/4 12:00:00
实施日期:1999/12/31 12:00:00
中国标准分类号:V11
国际标准分类号:49.025.10
引用标准:ASTM A 370-2012;ASTM E 112-2010;ASTM E 350-2012;ASTM E 381-2001;ASTM E 384-2011;SAE AMS-H-6875-1998;SAE AMS 2251;SAE AMS 2259;SAE AMS 2301K-2010;SAE AMS 2370;SAE AMS 2372;SAE AMS 2750;SAE AMS 2806;SAE AMS 2808;SAE AS 1182
适用范围:This specification covers an aircraft-quality, low-alloy steel in the form of bars and forgings. These products have been used typically for parts, such as nuts, bolts, and screws, 1.50 inch (38.1 mm) and under in section thickness, requiring a minimum tensile strength of 125 ksi (862 MPa) but usage is not limited to such applications.