SAE AMS 5617J-2006 12Cr、8.5Ni、1.2Ti和2.0Cu真空感应和真空自耗电极熔化溶液热处理、沉淀硬化的耐腐蚀钢棒材、线材和锻件

标准号：SAE AMS 5617J-2006
中文标准名称：12Cr、8.5Ni、1.2Ti和2.0Cu真空感应和真空自耗电*熔化溶液热处理、沉淀硬化的耐腐蚀钢棒材、线材和锻件
英文标准名称：Steel Bars, Wire, and Forgings, Corrosion Resistant 12Cr - 8.5Ni - 1.2Ti - 2.0Cu Vacuum Induction Plus Vacuum Consumable Electrode Melted Solution Heat Treated, Precipitation Hardenable UNS S45500
标准类型：V11
发布日期：2006/5/20 12:00:00
实施日期：1999/12/31 12:00:00
中国标准分类号：V11
国际标准分类号：49.025.10
引用标准：ASTM A 370-2005;ASTM A 370-2006;ASTM A 604-1993;ASTM E 45-2005;ASTM E 112-1996;ASTM E 353-1993;SAE AMS 2241P-2005;SAE AMS 2248F-2006;SAE AMS 2300K-2003;SAE AMS 2371G-2003;SAE AMS 2374D-2002;SAE AMS 2750D-2005;SAE AMS 2806B-2000;SAE AMS 2808D-2001;SAE ARP
适用范围：This specification covers two grades of a premium aircraft-quality, corrosion-resistant steel in the form of bars, wire, forgings, and forging stock. These products have been used typically for parts requiring corrosion resistance and high strength up to 800 °F (425mDC). The steel can be precipitation hardened to minimum tensile strengths up to 225,000 psi (1550 Mpa). Certain design and processing procedures may causes these products to become susceptible to stress-corrosion cracking after heat treatment; ARP 1110 recommends practices to minimize such conditions.