BS ISO 9924-1-2000 橡胶和橡胶制品.用热解重量分析法测定硫化和未硫化化合物的成分.丁二烯、乙烯－丙烯共聚物和三元共聚物、异丁烯－异戊二烯、异戊二烯和丁二烯橡胶

标准号：BS ISO 9924-1-2000
中文标准名称：橡胶和橡胶制品.用热解重量分析法测定硫化和未硫化化合物的成分.丁二烯、乙烯－丙烯共聚物和三元共聚物、异丁烯－异戊二烯、异戊二烯和丁二烯橡胶
英文标准名称：Rubber and rubber products - Determination of the composition of vulcanizates and uncured compounds by thermogravimetry - Butadiene, ethylene-propylene copolymer and terpolymer, isobutene-isoprene, isoprene and styrene-butadiene rubbers
标准类型：G34
发布日期：2001/4/15 12:00:00
实施日期：2001/4/15 12:00:00
中国标准分类号：G34
国际标准分类号：83.060
适用范围：1 This part of ISO 9924 specifies a thermogravimetric method for the determination of the total organic content, carbon black content and ash in vulcanizates and uncured compounds. The loss in mass at 300 ℃ is an approximate guide to the volatile-matter content of the compound. 2 The method is suitable for the analysis of rubber compounds and vulcanizates containing the following rubbers occurring alone or as mixtures: a) polyisoprene of natural or synthetic origin; b) polybutadiene; c) styrene-butadiene copolymers; d) isobutylene-isoprene copolymers; e) ethylene-propylene copolymers and related terpolymers. NOTE The field of application of the method may be extended to the analysis of compounds containing rubbers different from those given in this subclause, provided that the applicability of the method is tested beforehand using known compounds or vulcanizates having a similar composition. Other compounds are covered in ISO 9924-2. 3 The method is not suitable for rubbers containing polymers which form a carbonaceous residue during pyrolysis, such as many chlorine- or nitrogen-containing rubbers. 4 The method is also not suitable for materials containing additives which cause the formation of carbonaceous residues during pyrolysis, such as cobalt and lead salts or phenolic resins. 5 The method is not suitable for compounds containing mineral fillers, such as carbonates or hydrated aluminium oxides, which decompose in the temperature range from 25 ℃ to 650 ℃, unless suitable corrections based on prior knowledge of filler behaviour can be made. 6 The method is not suitable for the determination of the total polymer content of compounds or vulcanizates containing non-rubber organic ingredients that cannot be completely removed by solvent extraction carried out in accordance with ISO 1407.