SAE AMS 4613-2011 溶解热处理,冷加工(8%)和沉淀热处理工艺制备的6.3Cu-0.30Mn-0.06Ti-0.10V-0.18Zr铝合金薄板和厚板(2219-T87)

标准号：SAE AMS 4613-2011
中文标准名称：溶解热处理,冷加工(8%)和沉淀热处理工艺制备的6.3Cu-0.30Mn-0.06Ti-0.10V-0.18Zr铝合金薄板和厚板(2219-T87)
英文标准名称：Aluminum Alloy, Sheet and Plate 6.3Cu 0.30Mn 0.06Ti 0.10V 0.18Zr Solution Heat Treated, Cold Worked (8%) and Precipitation Heat Treated (2219-T87)
标准类型：V11
发布日期：2011/7/8 12:00:00
实施日期：1999/12/31 12:00:00
中国标准分类号：V11
国际标准分类号：49.025.20
引用标准：ANSI H 35.2-2009;ANSI H 35.2M-2009;ASTM B 594-2009;ASTM B 666-1990;ASTM B 666M-1990;ASTM E 8-2004;ASTM E 8M-2004;ASTM E 1409-2008;ASTM E 1447-2009;ASTM E 1941-2010;ASTM E 2371-2004;SAE AMS 2355;SAE AMS 2772-1997;SAE ARP 823;SAE AS 1990-1990
适用范围：This specification covers an aluminum alloy in the form of sheet and plate. These products have been used typically for parts requiring high strength up to 500 φF (260 φC), but usage is not limited to such applications. Material may be welded in the specified condition but properties are improved by reheat treatment after welding. Reheat treatment after welding, however, may reduce resistance to stress-corrosion cracking. Certain design and processing procedures may cause these products to become susceptible to stress-corrosion cracking; ARP823 recommends practices to minimize such conditions.